A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis
Само за регистроване кориснике
2019
Аутори
Čolović, BožanaJanković, Ognjenka
Živković, Slavoljub
Zizak, Zeljko
Zizak, Irina Besu
Jokanović, Vukoman
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice.
Кључне речи:
Calcium aluminate / Powders / Chemical preparation / Strength / Biomedical applicationИзвор:
Ceramics International, 2019, 45, 7, 9211-9218Издавач:
- Elsevier Sci Ltd, Oxford
Финансирање / пројекти:
- Хемијско и структурно дизајнирање наноматеријала за примену у медицини и инжењерству ткива (RS-MESTD-Basic Research (BR or ON)-172026)
DOI: 10.1016/j.ceramint.2019.01.266
ISSN: 0272-8842
WoS: 000463688500142
Scopus: 2-s2.0-85060930006
Колекције
Институција/група
Stomatološki fakultetTY - JOUR AU - Čolović, Božana AU - Janković, Ognjenka AU - Živković, Slavoljub AU - Zizak, Zeljko AU - Zizak, Irina Besu AU - Jokanović, Vukoman PY - 2019 UR - https://smile.stomf.bg.ac.rs/handle/123456789/2442 AB - The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice. PB - Elsevier Sci Ltd, Oxford T2 - Ceramics International T1 - A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis VL - 45 IS - 7 SP - 9211 EP - 9218 DO - 10.1016/j.ceramint.2019.01.266 ER -
@article{ author = "Čolović, Božana and Janković, Ognjenka and Živković, Slavoljub and Zizak, Zeljko and Zizak, Irina Besu and Jokanović, Vukoman", year = "2019", abstract = "The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice.", publisher = "Elsevier Sci Ltd, Oxford", journal = "Ceramics International", title = "A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis", volume = "45", number = "7", pages = "9211-9218", doi = "10.1016/j.ceramint.2019.01.266" }
Čolović, B., Janković, O., Živković, S., Zizak, Z., Zizak, I. B.,& Jokanović, V.. (2019). A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis. in Ceramics International Elsevier Sci Ltd, Oxford., 45(7), 9211-9218. https://doi.org/10.1016/j.ceramint.2019.01.266
Čolović B, Janković O, Živković S, Zizak Z, Zizak IB, Jokanović V. A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis. in Ceramics International. 2019;45(7):9211-9218. doi:10.1016/j.ceramint.2019.01.266 .
Čolović, Božana, Janković, Ognjenka, Živković, Slavoljub, Zizak, Zeljko, Zizak, Irina Besu, Jokanović, Vukoman, "A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis" in Ceramics International, 45, no. 7 (2019):9211-9218, https://doi.org/10.1016/j.ceramint.2019.01.266 . .