AB  - Purpose: To evaluate the influence of different surface treatments and metal primer application on bond strength of zirconia ceramic to a self-adhesive resin cement. Methods: 40 cylinder-shaped (empty set 12 x 5.25 mm high) of zirconia ceramic (Aadva Zirconia) were randomly divided into four groups (n= 10), based on the surface treatment to be performed: (1) Sandblasting with 125 mu m Al2O3 particles (S) (positive control); (2) Selective infiltration etching (SIE); (3) Experimental heated etching solution applied for 30 minutes (ST); (4) No treatment (C). Half of the zirconia specimens of each group received the application of Metal Primer II. Eight disks for each group were luted using a self-adhesive resin cement (G-Cem Automix) to composite overlays (Paradigm MZ100). After 24-hour storage (37 degrees C, 100% RH) bonded specimens were cut into microtensile sticks and loaded in tension until failure. Data were analyzed with two-way ANOVA and Games-Howell (P lt  0.05). Failure mode distribution was recorded and scanning electron microscopy (SEM) was used to examine the fractured microbars. The remaining cylinders of each group (n= 2) were used for SEM surface analysis. Results: Both surface treatments and Metal Primer IT application improved bond strength values (P lt  0.05). When Metal Primer II was not applied ST treatment achieved highest bond strength values (22.17 +/- 10.37 MPa). Sandblasting in combination with Metal Primer II enhanced bond strength values compared to the other groups (23.46 +/- 11.19 MPa). (Am J Dent 2012;25;269-275).
T2  - American Journal of Dentistry
T1  - Microtensile bond strength evaluation of self-adhesive resin cement to zirconia ceramic after different pre-treatments
VL  - 25
IS  - 5
SP  - 269
EP  - 275
UR  - https://hdl.handle.net/21.15107/rcub_smile_1689
ER  - 

@article{
author = "Casucci, Alessi and Goracci, Cecilia and Chieffi, Nicoletta and Monticelli, Francesca and Giovannetti, Agostino and Juloski, Jelena and Ferrari, Marco",
year = "2012",
abstract = "Purpose: To evaluate the influence of different surface treatments and metal primer application on bond strength of zirconia ceramic to a self-adhesive resin cement. Methods: 40 cylinder-shaped (empty set 12 x 5.25 mm high) of zirconia ceramic (Aadva Zirconia) were randomly divided into four groups (n= 10), based on the surface treatment to be performed: (1) Sandblasting with 125 mu m Al2O3 particles (S) (positive control); (2) Selective infiltration etching (SIE); (3) Experimental heated etching solution applied for 30 minutes (ST); (4) No treatment (C). Half of the zirconia specimens of each group received the application of Metal Primer II. Eight disks for each group were luted using a self-adhesive resin cement (G-Cem Automix) to composite overlays (Paradigm MZ100). After 24-hour storage (37 degrees C, 100% RH) bonded specimens were cut into microtensile sticks and loaded in tension until failure. Data were analyzed with two-way ANOVA and Games-Howell (P lt  0.05). Failure mode distribution was recorded and scanning electron microscopy (SEM) was used to examine the fractured microbars. The remaining cylinders of each group (n= 2) were used for SEM surface analysis. Results: Both surface treatments and Metal Primer IT application improved bond strength values (P lt  0.05). When Metal Primer II was not applied ST treatment achieved highest bond strength values (22.17 +/- 10.37 MPa). Sandblasting in combination with Metal Primer II enhanced bond strength values compared to the other groups (23.46 +/- 11.19 MPa). (Am J Dent 2012;25;269-275).",
journal = "American Journal of Dentistry",
title = "Microtensile bond strength evaluation of self-adhesive resin cement to zirconia ceramic after different pre-treatments",
volume = "25",
number = "5",
pages = "269-275",
url = "https://hdl.handle.net/21.15107/rcub_smile_1689"
}

Casucci, A., Goracci, C., Chieffi, N., Monticelli, F., Giovannetti, A., Juloski, J.,& Ferrari, M.. (2012). Microtensile bond strength evaluation of self-adhesive resin cement to zirconia ceramic after different pre-treatments. in American Journal of Dentistry, 25(5), 269-275.
https://hdl.handle.net/21.15107/rcub_smile_1689

Casucci A, Goracci C, Chieffi N, Monticelli F, Giovannetti A, Juloski J, Ferrari M. Microtensile bond strength evaluation of self-adhesive resin cement to zirconia ceramic after different pre-treatments. in American Journal of Dentistry. 2012;25(5):269-275.
https://hdl.handle.net/21.15107/rcub_smile_1689 .

Casucci, Alessi, Goracci, Cecilia, Chieffi, Nicoletta, Monticelli, Francesca, Giovannetti, Agostino, Juloski, Jelena, Ferrari, Marco, "Microtensile bond strength evaluation of self-adhesive resin cement to zirconia ceramic after different pre-treatments" in American Journal of Dentistry, 25, no. 5 (2012):269-275,
https://hdl.handle.net/21.15107/rcub_smile_1689 .